Figure "Fretting threatened engine parts" (Ref. 6.2-12): Engine components that are typically affected by fretting (compare with Fig. "Fretting zones in an aeroengine"). These indicate the multifariousness and frequency of this problem.
Fan blades with short chord lengths are used in older engine types. These blades are strengthened by clappers and snappers in the top half of the blade (“1”). The surface pressure on the clappers during impact fretting is between 7 and 70 MPa, which can cause fatigue fractures with serious consequential damages. This oscillation stress can cause the clapper plug or blade leaf to fail.
The same is true for turbine rotor blade shrouds. The slim blades of the low-pressure turbine that support one another with shrouds are especially sensitive (“2”). Wear occurs at the lay-on surfaces with the most tension (Fig. "Fretting wear at turbine blade shrouds") and can therefore lead to a drop in tension and increased oscillation stress. Worn out shroud assemblies are susceptible to the shrouds gliding over one another (shingling), which can cause blade failures.
The classic fretting damage zone is in the lay-on surfaces of the compressor and turbine rotor blades (“3”) and the corresponding disk slots (Figs. "Failed rotor blade inside the engine", Fretting influence seen at crack types" and "Fretting surface cracks at contact").
Fretting can also be observed in the lay-on surfaces of guide vanes. Metal removal in the housing (Fig. "Fretting wear at compressor guide vanes") and the mutual contact surfaces of the blades (“4”) lead to a change in the blade angle (danger of a worsening of compressor performance, stalls, oscillations) and in extreme cases the blade breaking out of the housing slot (Fig. "Fretting wear at compressor guide vanes").
To prevent axial travel, rotor blades must be secured in the disk slots. If this is done with metal sheets, wire rings, or labyrinth mounts (“5”), the lay-on surfaces at the edge of the ring as well as the front of the blade can be affected by fretting and cracks (Fig. "Fretting by vibration of blade fastener").
Threaded connections (“6”) can be subjected to fretting wear on all lay-on surfaces, depending on stiffness. This can be especially dangerous if the highly dynamically stressed screw shaft is damaged by fretting (e.g. in fitted bolts) or if fretting occurs in the highly stressed disk bore and creates an dynamic crack (Fig. "Fretting damage at turbine rotor").
Cushioning damping wires (damping rings ) are used to avoid high-frequency oscillations. These are inserted into an internal slot of the rotating part, and the centrifugal force provides sufficient pressure. A further type (e.g. in axial turbine disks of turbochargers and older industrial gas turbine types) of friction damping is drawing a slitted or segmented damping wire through the blade leaf. The intended friction between the damping wire and the applied part leads to strong fretting in the slot, i.e. the bore and its ring. This stress should be taken into account by the designer.
Threaded flange behaves similarly to threaded connections (“7”, Figs. "Fretting damage at turbine rotor" and "Fretting wear at compressor guide vanes"). Insufficient stiffness leads to pronounced friction wear, loosening, and fatigue fractures.
Multiple splinings are used to connect rotor shafts and as plug connections for auxiliary drives (Ills. 6.2-19 and 6.2-20). If the splining is not sufficiently lubricated and/or the connection is poor (e.g. misaligned), it will result in considerable wear. In extreme cases there is a complete failure of the momentum transfer - the connnection “runs through”.
Heavy fretting is common in roller bearing seats (“9”, Figs. "Fretting wear between bearing and titanium shaft" and "Fretting wear at spline couplings") with insufficient stiffness, poor fastenings, or a oil-damped snap-through bearing suspension. Configurations in which the bearing ring (steel) is seated directly in a titanium surface are especially prone to wear.
Combustion chambers and gas baffles (“10”) are usually subject to strong vibrations and relative movements caused by thermal strain. This puts so much wear stress on the plug connections (Fig. "Fretting at combustion chambers"), that the amount of metal removal becomes a deciding factor in the life span of the part.
Clamp fastenings can wear through and break pipes if they are loose or the material combination is poorly chosen (“11”).
Guide vane adjusters (“12”) have a multitude of constantly lubricated joints and bearings that vibrate strongly during operation and/or make small adjustment movemnts. Because these parts are outside the engine, they are prone to corrosion. These conditions promote fretting.

Figure "Failed rotor blade inside the engine": In an older, single-engine tactical aircraft, a rotor blade in the front compressor stage suffered a fatigue fracture. The crack initiated in the fretting zone in the blade root (details “A” and “B”). The material, a type of 13% Cr steel, is relatively resistant to dynamic strength losses due to fretting, but the damage occured due to other factors that promoted it:
Unfavorable engine operation. In all likelihood, there was a long idle during the start phase. Additionally, the crack inspection during an overhaul was not optimal, making recognition of initial cracks difficult.
In similar cases, signs of improper shot peening (the angle was too shallow) during overhaul were observed. During shot peening, crack-like overlapping was created with insufficient hardening (lower compressive stress and less peen hardening)
It is interesting to note that the primary, hook-shaped bent (detail “B”) blade fragment was caught in the following guide apparatus in many cases, preventing it from traveling through the engine and minimizing consequential damages.
The size of the remaining fractured surface “FG” in relation to the fatigue fractured surfaces “FS” corresponds to the static stress (mean stress of centrifugal force and gas flexural stress) of the blade root. If the remaining surface is relatively small, then the static stress was low. This increases the chance of success of remedies that optimize the tribo-system.
The size of the remaining fractured surface in rotor blades is relatively small (especially in titanium alloys). This can be explained by the designed low levels of static stress (Fig. "Fretting surface cracks at contact") and must take fretting damage into account.

Figure "Fretting influence seen at crack types": A typical weak point of compressor rotor blades are the lay-on surfaces and the areas near a dovetail root in a disk slot (Ref. 6.2-12). High-frequency blade oscillations (“A”) and/or low-frequency expansions with centrifugal force changes (“B”) can create micro-movements with typical wear signs, so-called Fretting wear (oscillation friction wear, fretting corrosion, etc.). This wear is especially dangerous because it weakens the blade material. It promotes fretting fatigue with crack initiation (arrows) and/or an increase in stress levels (equivalent stress during thrust and normal stress, see Fig. "Fretting load parameters in dovetail") in the areas surrounding the contact surface that do not seem directly affected (arrow).
Unusual fretting types can indicate unusual operating conditions. These wear images give important clues as to the damage causes and thus help in designing remedies.
A sign of the damage intensity is the length of the wear tracks (a) in the micro-region. The total width of the wear track must not be confused with the movement amplitude. It can be discerned by microscopically analyzing the damaged surface.
The location of fatigue cracks in relation to the fretting zone gives clues as to the damaging of the surface, stress, and load distibution:

• Macro-cracks and fractures that are outside of the fretting zone in the blade shaft (“1”) indicate acceptable behavior of the tribo-system towards the damage. Evidently there is high fretting stress in the crack initiation zone. In these cases, the first step should be to determine whether or not this area was shot-peened in accordance with regulations. If the peened surface shows defects, appropriate measures must be taken. In this case, the incubation time is not dependent upon the wear damage.

• Micro-cracks in the fretting zone (“2”) are observed in metallic protective layers and/or in the base material. They are a sign of a clearly damaging influence on the dynamic stress and relatively low static stress. Although cracks can initiate in the stressed time frame, they do not progress dangerously.

• If there are macro-cracks at the edge of the fretting zone (“3”), it indicates high stress and a high coefficient of friction between the contact surfaces. In this case it must be determined whether or not a glide layer and/or sufficient shot peening (calotte topography) were applied. It is important to ascertain whether the glide coating or other protective intermediate layers change unpermissably under operating conditions (time, temperature, surface pressure). The oxidation of metallic intermediate layers can create brittle and hard oxides that act very abrasively. Signs of galling indicate cold fusing or sticking due to metallic contact. In this case, there was obviously no sufficient glide layer.High coefficients of friction can also be created by dust forcing its way between the contact surfaces. The fretting surfaces around the crack should be subject to a micro-analysis for these indicators.
  

• Macro-cracks and fractures in the fretting zone (“4”) indicate definite damage of the material with a large drop in strength. These cracks can form from the micro-cracks described in “2” if, for example, the load levels increased or the time frame enabled the cracks to expand (e.g. creeping or oxidation).

Figure "Fretting surface cracks at contact" (Ref. 6.2-6): Under relatively low bending loads in a blade root, unexpanding micro-cracks of about 0.1 mm (“1” detail) can form in the wear surfaces. These micro-cracks are often observed in practice (see Ref. 6.2-1). The crack expansion depends on the stress levels as determined by design and centrifugal force. The diagram (the ordinate is the bending amplitude, the abscissa is the static centrifugal stress, i.e. mean stress) is based on calculated estimates and spot tests. It shows the capability for expansion of a 0.05 mm crack in a 13% Cr steel blade with typical root geometry. It is shown that micro-cracks initiate at low bending fretting loads before they expand into macro-cracks (detail “2”). Evidently no macro-cracks occur in the region between the two curves.
This insight also corresponds to new thoughts about the dynamic strength-increasing effect of pressurized residual stresses near the surface (Ref. 6.2-7), for example those achieved through shot peening.
“…the non-expanding cracks have been known for a long time…the crack closed as force decreased but before it reached zero. In this manner, the crack only opened again when the force was considerably above zero during following small amplitudes. This also means, however, that the effective stress amplitude or…fracture mechanical…the effective stress intensity factor was minimized as the most important parameter for the dynamic strength…The cause of the crack closing is the residual stress created by the treating process.”
This also explains the observation that overlappings of the type created shot peening at a low angle do not always lead to dangerous crack expansion. For the same reason, damaged blade roots can be regenerated through shot peening, even if micro-cracks (that could not be found during serial non-destructive inspection) cannot be removed.
Understandably, the more a material tends to hardening and creation of pressurized residual stresses, the greater the dynamic strength-increasing effect is. In line with experience, steels behave more advantageously than titanium alloys (Fig. "Fretting at titanium alloys").
If the operating loads in the wear zone (temperature and stress) are large enough that the residual stresses are noticeably reduced by creeping effects over operating time, the protective influence of hardening is reduced accordingly. This is followed by the micro-cracks growing. For this reason, it may be important to renew the hardening at specific time intervals (maintenance intervals), which is common practice. It is important that the intervals are sufficiently short. Comparable residual stress measurements during the development stage can assist in determining the interval length.
Interestingly, the usable dynamic strength is not dependant upon centrifugal stress at levels above those characteristic for the configuration and the tribo-system (in this case, roughly 100 N/mm²).
From this it can be concluded that dangerous crack expansion in the fretting zone requires limiting of the bending loads. This relatively low value depends on the individual design.
If the centrifugal stress in the blade root is relatively high, the blade root loads must be lowered considerably below the critical value to avoid fractures due to fretting (see also Fig. "Failed rotor blade inside the engine").

Figure "Fretting by vibration of blade fastener": Rotor blades in compressors and turbines are affected by axial forces consisting of gas loads, disk vibrations, thermal distortion, and misaligned lay-on surfaces (see Fig. "'Blade walking' by axial forces"). Therefore, the blades must be fixed axially in both directions. This results in limited areas of the blade laying against fasteners (e.g. rings, spacers, labyrinth mounts, disk annulus), at least for a short time. In this case, differences in stiffness will result in fretting movements. These movements can be caused by oscillations in the blade and/or the surface it is in contact with. The diagram depicts a case in which vibrations of a labyrinth mount (top left diagram) led to fretting wear in the area laying against the blade root (top right diagram). This resulted in sharp-edged depressions forming in the labyrinth mount, and the stress concentration in these combined with the oscillation stress initiated cracks (bottom diagrams). A microscopic analysis of the fretting marks on the blade root indicates the oscillation amplitude (“S₂”) and thus gives important clues as to the nature of the oscillations (size, form) in the labyrinth mount. This is an important requirement for the designing of remedies and calculation of risk assessment.

Figure "'Blade walking' by axial forces": Damages of the type in Fig. "Fretting surface cracks at contact" show that, under certain conditions, turbine rotor blades can travel against the flow (bladewalking) or, as the case may be, the pressure loss in the disk slot (in axial direction). In turbine blades, this movement is against the gas flow (forwards, see also Fig. "Coefficient of friction during relative motion"), in compressor blades in direction of the gas flow (rearwards)
The diagrams are of two hypotheses that explain this phenomenon. It may be that both of these possibilities act in combination. In both cases, high frequency oscillations of the blade leaf are assumed (base flexure).
The hypothesis shown in the top right diagram assumes coupled oscillations of a turbine disk and blades. Gas and mass forces take effect, depending on the oscillation deflection, which periodically causes a movement against the gas flow. The mechanism is similar to that in the top left diagram. The figure climbs up the periodically stressed string against gravity through alternating clamping force (frictional force).
The deflection of the blade annulus should be between 10² - 10³ mm. A certain combination of forces and movements in the root region causes the oscillating blade (Fig. "Fretting by vibration of blade fastener") to lay against the labyrinth ring (bladewalking). This is where the observed friction wear occurs. If, under certain circumstances, the coupled blade/disk oscillations “stand still” and run around with the rotor, corresponding fretting wear on the hold surface will appear periodically around the circumference.
The bottom diagram depicts a hypothesis that is based only on blade oscillations. It has been observed that, if these are powerful enough, they can lower the friction force in the blade root so much that even a small axial force will cause the oscillating blade to travel. This axial force can be explained by the disk warping due to temperature gradients, even if they are very minor. In compressor disks, the rear side of the disk is assumed to be warmer, which causes the disk to warp and offsets the annulus to a sufficient degree that the blade experiences a rearwards pull against the increased gas pressure.
In the (uncooled) turbine disk it is typically the front side that is warmer, warping the disk so that the pull is in a forward direction, i.e. against the gas pressure. In this hypothesis, the blades stay in their axially changed position. Therefore only the individual oscillating blades should leave fretting marks on the hold surface.

Figure "Fretting damage on titanium disk" (Example "Fretting damage on titanium disk", Ref. 6.2-1): Fretting in disks usually occurs in high-stress zones such as threaded bores, flange overlays, and centering collars. The high stress levels in these zones create the possibility of dangerous crack expansion. The limited possibilities for inspection of bores add to the difficulties. Because of this, the dynamic strength-reducing effect in the fretting zones is especially important in this case and must be taken into account by the designer.
Coating areas that are susceptible to fretting (Ref. 6.2-5) with plasma spray-coatings or galvanized coatings is possible, but very problematic. First it must be proven that the coating itself does not lower the dynamic strength of the part to a unallowable degree. This effect can result from the application process (e.g. strength/stiffness drops due to thermal changes, hydrogen-embrittlement) or the coating itself (e.g. brittleness, crack initiation, low dynamic strength).
A tribo system with outward-facing open cracks is clearly affected by intruding media. Typical damaging media are sea atmosphere and condensation water.
Remnants from the manufacturing process or lubricants that break down into aggressive components at high operating temperatures must be taken into account. Various oxides and other reaction products can form inside cracks, fundamentally changing the behavior of a tribo-system (see also Fig. "Wear products influencing fretting"). These factors must be considered during technical trials and verification of the operational capability of tribo-systems.
Bores are usually hardened by shot peening or “piercing” (chapter 6.3)

Figure "Fretting damage at turbine rotor" (Ref. 6.2-1): This case concerns an older engine type. The areas affected by fretting are the flange lay-on surfaces and the bolt bores, both of which are most likely subject to relative micro-movements. In this situation, it is not a screw connection that firmly fastens parts together, but rather an anti-twist device. Warping occurred internally through the hollow shaft that acts as a bushing.
Fatigue cracks initiated in the bolt bores of a low-pressure turbine disk. The disk material is 13% Cr steel.
The cracks started in fretting zones of the flange supporting surface and from cylindrical surfaces of the bolt bores. There were two typical areas where cracks initiated (bottom detail): the edge of bevel “1” and in the axial center of the cylindrical surface “2”. Along with the micro-cracks, areas with macro-cracks and a typical bow-shaped progression also appeared in the fretting zone.
This example shows that this type of anti-twist device without braced flange surfaces are susceptible to fretting and should therefore be avoided.

Figure "Fretting wear at compressor guide vanes": The connection between guide vanes and the casing or supporting intermediate structures are typical fretting zones. Not only the unavoidable blade oscillations must be observed, but also differences of thermal expansion between casings and blades. Different thermal expansion and/or temperature differences cause the connection to loosen, if only for a short time, allowing glide wear and impact wear to occur. These influences must be considered when testing a tribo-system and can affect the selection of possible coating materials. Although dynamic cracks are less likely in the roots of guide vanes than in rotor blade roots, they can still occur, and the geometric wear can offset the blade. If this happens, the blade may come into contact with the rotor. In extreme cases the blade or blade segment may fall out.
For this reason, even new parts made of titanium alloys in fretting-susceptible zones should be armored with an anti-wear coating (e.g. tungsten carbide).

Figure "Failing of retaining bolts at contact areas" (Ref. 6.2-8): Turbine guide vanes are affected by high perimeter forces from gas deflection. The rotation of the guide apparatus in the casing is avoided through detachable fastenings. These fastenings are subject to strong static forces, part-specific vibrations, and thermal strain. This leads to micro-movements at the contact areas to the guide apparatus. There are several structural solutions to this problem. In the case at hand, 44 so-called “anti-rotation pins” were used. In modern engines, there are catches on the shrouds of the guide vane segments that fit into corresponding recesses in the casing.
If these fastenings fail, engine failure can be expected. In extreme cases, the guide apparatus rotates in the housing, grinds through the casing wall, and throws fragments out of the engine (Example "Failing retaining bolts 1" and Example "Failing retaining bolts 2").

Figure "Fretting wear at turbine blade shrouds": Turbine rotor blades are equipped with shrouds, which support and dampen to prevent vibrations. Fretting wear at the bearing surfaces of the shrouds (top left diagram) can affect their life spans. Therefore, the wear resistance of the bearing surfaces is increased by welding on armor (usually a stellite).
The damage mechanism can be either gliding wear and/or hammering wear (Fig. "Load-specific wear types").
Experience has shown that a change in the blade material can have a strong influence on shroud wear, especially if the change is from a polycrystalline cast material to a single crystal material. This may be due to different wear behavior of the new material in unarmored bearing surfaces. The wear could also be connected to increased blade oscillations and/or stiffness changes due to the change in the modulus of elasticity.
Heavy fretting wear causes tight shrouds to loosen, “overriding” (top right diagram), and fatigue crack initiation with shroud breakouts (bottom diagram). The reduction in shroud tension and increased relative movements accelerate the wear damage and promote fatigue fractures in the blade leaf or shroud.

Figure "Fretting at combustion chambers" (Ref. 6.2-4): Combustion chambers are subjected to vibrations around 100 Hz due to the pressure changes from combustion. Hot parts, especially combustion chambers, also have many plug connections with the surrounding parts to counterbalance changes in thermal expansion. The top diagrams show a pipe combustion chamber from an older military engine with typical plug connections:

• The plug connection at the gas outlet to the turbine (“1”) serves to seal the hot gases.
• Guide sheets (“2”)
• Mountings to the casing (“3”, also see bottom diagram)
• Connected openings (ignition) to the other combustion chambers.Super alloys create wear-reducing oxides under favorable conditions (Fig. "Wear products influencing fretting"). This makes them fairly wear resistant. Operational experience determines wether or not they require additional anti-wear coatings. If the wear is very heavy, hard coatings such as WC-plasma spray coatings are used.
  

The problem of fretting in combustion chambers and hot gas pipes is especially serious in “Low-NOx” combustion chambers due to their typical flame instability (flickering) and corresponding pressure changes with vibrations.

Figure "Fretting wear induced fir tree cracks": Wear is an important factor for the life span of engine parts and a determining factor for the cost of overhauls and repairs. Usually, the repairable wear damages are exactly specified in overhaul manuals and allowable repair methods also given. Determining these specifications and manuals requires a profound knowledge of the stress levels and repair processes, as well as their possible effects on operating properties.
An important criterion is the repair and permissibility of geometric changes through metal removal. It must be remembered that overhaul and repair involves fusing new parts to run-in ones. The contact surfaces must guarantee safe functioning of the part during the new interval of operation. If a new surface is fused with an unevenly worn one, there must be no unpermitted tension concentrations or load changes.
In the case shown, the turbine blade roots were slightly shorter than the disk width (tolerances of the blade root width and the fastening elements, mounting tolerances). A “nose” formed on the disk slot due to metal removal (bottom diagram). After the old blading was replaced with a new assembly, the blade roots lay against these “noses”. Centrifugal force then created strong bending loads in the fir-tree slots of the disk, causing cracks to initiate in the upper disk slot (top right diagram). It is also important to ensure that, when setting overhaul guidelines (manuals, specifications), the metal removal from contact surfaces is given extra attention, if new contact surfaces are to be combined with old ones (e.g. during a modulus replacement).
This problem occurs especially in the following parts:

• Blade roots and disk slots when replacing the blading or individual blades.

• Shaft connection splining (Fig. "Failure due to fretting wear at spline coupling"), for example, when replacing auxiliary units such as starter generators or pumps.

• Replacing fastening bolts or parts with fixing studs (e.g. guide vane segments, see Fig. "Failing of retaining bolts at contact areas").

Figure "Jamming by fretting": Guide vane adjustment systems are affected by fretting wear. This is due primarily to their filigreed design and the large number of moveable parts with joints and bearings. The system can be made to vibrate at high frequency by the blading and casing. Because the adjustment systems are mounted in the bypass duct or outside of the engine, corrosive atmosphere (e.g. ocean air) can affect them even during operation. Because they require good glide qualities, strict tolerances (guaranteeing zero-backlash), and abrasion resistance, the joint elements must be made of steel. These are not corrosion-proof, not even 13% Cr steels. The various operating loads that act on a guide vane adjustment require combining very different materials, including steel, titanium alloys, Mg or Al alloys, and glide materials, such as synthetics and bronze. The use of unsuitable auxiliary materials during assembly and maintenance (cleaners, lubricants) or unusual operating conditions (e.g. long standing times in corrosive environments with large temperature changes and/or high dust levels) can promote the creationg of reaction products at the contact areas. In this way, the fretting behavior of a tribo-system can become worse over time.
Experience has shown that fretting can result in glide surfaces jamming and getting hung up. This can result in fractures of part regions under high stress (bottom diagram).
Similar wear conditions can also affect different engine systems (e.g. thrust reverser, Fig. "Fretting wear at titanium with steel contact").
A special problem is posed by the glide bearings of the central pin in guide vanes being rubbed out or sticking fast (Example "Variable stator vane bushings"). Synthetic bushings can swell and jam due to condensation water or unsuitable cleaning materials. If they are not properly lubricated, synthetics filled with inorganic materials (e.g. fiberglass) are susceptible to the trunnion being worn down severely, increasing play to dangerous levels. Overly high operating temperatures cause embrittlement and crack initiation or shrinking of the bushing.
The suitability of a part must be verified in trials that sufficiently simulate operating conditions before it is serially implemented. These trials are very time-consuming, since combined factors such as wear, corrosion, and aging (temperature cycles) cannot be temporally accelerated.

Figure "Wear in protective sleeves": Under unfavorable conditions, guides of control cables and flexible shafts are subjected to strong abrasive wear by gliding and hammering movements. When transferring large amounts of momentum, flexible shafts tend to offset and vibrate inside the conduit. In extreme cases, glide layers or lubricants are broken through and wear soon begins to affect the part`s ability to operate. It was observed that a vibrating flexible shaft of steel wire exerts a powerful hammer stress on the softer cladding tube (e.g. 18 9 CrNi steel or titanium alloy). The cladding tube was drawn out to the point that it lengthened several millimeters. The resulting warping and vibrations can lead to pipes fracturing and the system failing.

Figure "Fretting wear at lever joints": As mentioned in Fig. "Jamming by fretting", adjustment- and blocking systems in thrust reversers are subject to high fretting stress and corrosive influence; the latter can be observed most frequently on adjustment bearings (bottom diagram). If wrong (unsuitable) cleaning materials and lubricants are used in this area during maintenance, the joints can lock up. One situation that has been shown to be problematic is when glide coatings containing MoS₂ come into contact with ocean atmospheres. Degreasing constantly-lubricated joints and bearings during maintenance (e.g. with unsuitable sprays) or overhaul (e.g. hot degreasing-baths) can gravely accelerate this process.
The top diagram is a schematic of a mechanical blocking system in a military thrust reverser. Extra attention should be paid to the material combination of the lock pin and the lead-through. The hammer stress typical to this part can, in a very short time, lead to abrasive wear in many different areas (“1” to “5”), causing the part to weaken and fracture or dangerously increase the amount of play. An effective remedy is an elastic bracing of the opened flap over a flexible seal.

Figure "Fretting wear at titanium with steel contact" and Figure "Fretting wear between bearing and titanium shaft": Even under seemingly ideal lubricating conditions, titanium alloys tend to extreme metal removal during high-frequency vibrations against steel surfaces. Typical situations include roller bearing seats in casings (Fig. "Fretting wear at titanium with steel contact", Ref. 6.2-12) or on titanium-alloy shafts (Fig. "Fretting wear between bearing and titanium shaft"). In only a few hours, several milimeters of metal were removed from a titanium-alloy bearing casing in which an oil-damped bearing ring was set (see also Ref. 6.2-14; top diagram). However, the steel ring showed no measurable wear. It is typical that markings stamped into the front surface of the bearing ring were negatively embossed in the titanium surface (center diagram). The problem was finally solved by applying an anti-wear coating in the form of a tungsten carbide cobalt plasma spray coating to the contact surfaces of the titanium part.

Under similar circumstances, an inner bearing ring on a titanium shaft loosened. Fretting wear combined with an oil feed led to the bearing ring loosening and running through, destroying the shaft. In this case, as well, the bearing ring seat in the shaft was successfully protected with a WC-Co-layer.
These damages indicate that the abrasion process is actually promoted by the oil between the contact surfaces. Whether or not this effect is due to the wear products being transported out of the “pumping” gap between the contact surfaces has not been determined.

Figure "Fretting wear at spline couplings": Detachable shaft couplings in the form of interleaved plugs are often used in engines. This design principle is applied in main shafts and auxiliary units (top diagram, “1” to “6”). These shaft connections are extremely reliable if the following conditions are met:

• suitable material combination (tribo-system)
  

• sufficient lubrication-limited vibrations (e.g. torsion vibrations)
  

• proper alignment of the rotating components.

• tuned stiffness, in order to minimize relative movements in the interleaving

• no overstress during operation (e.g. through impact stress), i.e. correct design that reflects operating conditions

If any of these conditions are not met, wear in the interleaving can be expected. This often remains unnoticed until the coupling ceasses to mesh (Fig. "Failure due to fretting wear at spline coupling", Refs. 6.2-3 and 6.2-12).

Figure "Failure due to fretting wear at spline coupling" (Ref. 6.2-3, Example "Increased wear caused by incorrect machining"): Auxiliary components such as hydraulics, fuel pumps, oil pumps, and starter generators are usually powered via a so-called radial shaft from the main engine shaft to the auxiliary transmission. These often use tight and moveable interleaved plugs to connect the gears to the shafts and auxiliary components. The above mentioned example describes the typical damage symptoms when one of these connections fails due to extreme fretting in the splining.