dangers-of-residual-stressesWarpingRubbing of a compressor housing throughwarping of the new parts during the firststartupLCF crackinside the partDynamic fatigue in the LCF rangeDynamic fatigue crack in a turbine disk,promoted by high residual stresses Stress corrosion crackingCracks in the grinding surface ofa toothed gear through high tensileresidual stresses during burnishing Hydrogen embrittlement anddelayed cracking Dangers of residual stresses:Repair welding on a compressoroutlet housingOxygen absorption(embrittlement),strength losses,structural changes,residual stressesRubbing areaOverheatedhousing wallStress corrosion cracking under the chromecoating after burnishingHeat-treatable steelChrome coatingCrack welded shutRenewed cracking